LT·J506 2.0/2.5/3.2/4.0/5.0 mm Carbon Steel Electrodes
Specification:AWS E7016 is low hydrogen potassium coating carbon steel electrode. It has good welding technological properties and AC arc stable, low spatter, beautiful appearance of weld, good slag detachaility and all position welding. Weld metal has excellent plasticity, low temperature-tenacity and anti-crack ability.
Conform to Standard
GB/T 5117 E5016
AWS A5.1 E7016
ISO 2560-B-E 49 16 A
Purpose:It is applied in welding medium-carbon steel and low-alloy structures such as 16Mn, 09Mn2Si, 09Mn2V and the steels used in shipbuilding such as A, B, D, E.
Attention:
1. It is easy to expose to moisture, please keep it in dry condition.
2. It needs heating for 1 hour under the temperature 350C before using.
3. It requires basis metal clearing impurities(such as oil, rust, water and so on)
4. Use short ARC, narrow-circuit method for welding
Chemical Composition(%)
| Chemical Composition |
C |
Mn |
Si |
S |
P |
Ni |
Cr |
Mo |
V |
| Guarantee Value |
≤
0.15
|
≤
1.60
|
≤
0.75
|
≤0.035 |
≤0.035 |
≤
0.30
|
≤
0.20
|
≤
0.30
|
≤
0.08
|
| General Result |
0.080 |
1.05 |
0.51 |
0.012 |
0.020 |
0.012 |
0.030 |
0.007 |
0.016 |
Mechanical Properties of Deposited Metal
| Test Item |
Rm(MPa) |
ReL(MPa) |
A(%) |
KV2(J) |
| -20℃ -30℃ |
| Guarantee Value |
≥490 |
≥400 |
≥20 |
≥47 |
≥27 |
| General Result |
540 |
430 |
32 |
175 |
169 |
X-Ray Radio-graphic Test Requirements:Grade I
Reference Current(AC,DC+)
| Diameter(mm) |
Φ2.5 |
Φ3.2 |
Φ4.0 |
Φ5.0 |
| Amperage(A) |
60~100 |
80~140 |
110~210 |
160~230 |
Notes:
1. The electrode must be preheated at the temperature of 350°C for 1 hour. Preheat the rod whenever it is used.
2. The impurities such as rust, oil stains and moisture must be cleared off of the work piece.
3.Short arc is required to perform welding. Narrow weld path is preferred.